李珠1，张婷2，刘元珍1

（1 太原理工大学土木工程系， 太原 030024； 2 赛鼎工程有限公司， 太原 030032）

［摘要］对保温结构新体系——玻化微珠保温墙模复合剪力墙体系中的高剪跨比剪力墙进行低周往复荷载试验研究。通过对比试验的方法，研究了保温墙模复合剪力墙与普通实体剪力墙在承载力、刚度、延性等方面的性能。试验结果表明:复合剪力墙的承载力较普通剪力墙的仅降低约7%，而刚度却明显减小，既使结构有较高的安全储备，又使延性得到明显改善，该体系在结构抗震方面能发挥较大潜力；墙模与内部混凝土的粘结能力强，共同工作性能良好。研究成果可以作为保温墙模复合剪力墙工作性能评价与工程设计的理论依据。

［关键词］高剪跨比复合剪力墙； 低周往复荷载试验； 承载力； 刚度； 延性

中图分类号：TU317+1文献标识码：A文章编号：1002848X(2013)07000504

Research on low-cyclic load test of large shear span ratio composite shear wall with GHB heat preservation formwork

Li Zhu1, Zhang Ting2, Liu Yuanzhen1(1 Department of Civil Engineering, Taiyuan University of Technology, Taiyuan 030024, China;2 SEDIN Engineering Co., Ltd., Taiyuan 030032, China)

Abstract:A low-cyclic load test was carried out on large shear span ratio composite shear wall structures with heat preservation formwork by glazed hollow bead (GHB), which is a kind of new insulation structure system. The test was conducted to compare the performance of composite shear wall and ordinary solid concrete shear wall in terms of bearing capacity, stiffness and ductility. Results show that compared with ordinary solid concrete shear wall, the stiffness of composite shear wall reduces significantly while the bearing capacity reduces about 7%. Composite shear wall is characterized by higher safety reserve and significantly better ductility, which indicates this composite shear wall has greater performance in seismic design. The test results also demonstrate that the formwork of composite shear wall works together with internal concrete as a whole. Study results can be applied in design and performance evaluation of composite shear wall structure with heat preservation formwork.

Keywords:large shear span ratio composite shear wall; lowcyclic load test; bearing capacity; stiffness; ductility

*国家自然科学基金项目(50778118)，教育部高等院校博士点基金项目(200801120003)，高等院校博士点基金项目(20101402120007)。

 作者简介：李珠，博士，教授，博导，Email：lizhu9999@vip.sina.com。

参考文献

［1］陈万山，杨德健. 带缝空心保温剪力墙变形性能试验研究［J］. 建筑结构，2010，40(S2)：404408.

［2］左晓宝. 带竖缝钢筋混凝土剪力墙的抗侧刚度分析［J］. 力学与实践，2003，25(3)：4648.

［3］康胜，曾勇，叶列平. 双功能带缝剪力墙的刚度和承载力研究［J］. 工程力学，2001，18(2)：2734.

［4］刘元珍，李珠. 保温墙模复合剪力墙试验研究［J］. 太原理工大学学报，2008，39(2)：167170.

［5］刘元珍，李珠. 保温墙模复合剪力墙轴心受压性能研究［J］. 西安建筑科技大学学报：自然科学版，2008，40(3)：341347.

［6］刘元珍，李珠，杨卓强. 不同参数带缝剪力墙非线性分析［J］. 工程力学，2009，36(SⅠ)：4550.

［7］董宏英. 带暗支撑双肢剪力墙抗震性能试验及设计理论研究［D］. 北京：北京工业大学，2004.

［8］盛光远. 粘钢加固钢筋混凝土剪力墙抗震性能研究［D］. 上海：同济大学，2006.