吴瑾¹，王东东¹，吴方华²

（1 南京航空航天大学土木工程系，南京 210016；2 锦宸集团有限公司，南京 210037）

 

［摘要］通过10块不同钢筋腐蚀率、100%再生骨料取代率的再生混凝土简支板静力试验，研究腐蚀钢筋再生混凝土板破坏形态、承载力及跨中挠度。根据试验结果研究了再生混凝土板的承载力和挠度与钢筋腐蚀率的关系，并提出了腐蚀钢筋再生混凝土板承载力计算公式。

［关键词］腐蚀钢筋；再生混凝土板；破坏形态；承载力；挠度

中图分类号：TU375.2        文献标识码：A        文章编号：1002-848X(2013)01-0069-04

 

Wu Jin¹, Wang Dongdong¹, Wu Fanghua²

（1 Department of Civil Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China; 2 Jinchen Group Co., Ltd., Nanjing 210037, China）

 

Abstract: Based on the static experiments of 10 simplesupported recycled concrete slabs with different steel corrosion degree and 100% recycled aggregate, the failure mode, bearing capacity and mid-span deflection of recycled concrete slabs with corroded reinforcing bars were investigated. According to the results, the relationships between bearing capacity and deflection of recycled concrete slabs and steel corrosion degree were established. The calculation formula for bearing capacity of recycled concrete slabs with corroded reinforcing bars was put forward.

Keywords: corroded reinforcing bar; recycled concrete slab; failure mode; bearing capacity; deflection

　*国家自然科学基金项目（51279074）

作者简介：吴瑾，博士，教授，Email：wujin@nuaa.edu.cn

 

［1］肖建庄.再生混凝土［M］.北京:中国建筑工业出版社，2008.

［2］刘冠国.钢筋混凝土锈蚀构件性能试验研究［D］.南京:河海大学，2006.

［3］卞汉兵.海洋环境锈蚀钢筋混凝土板试验研究及理论分析［D］.南京:河海大学，2003.

［4］李富民,袁迎曙.腐蚀钢绞线预应力混凝土梁的受弯性能试验研究［J］.建筑结构学报，2010,31(2):78-84.

［5］吕维波.9年期锈蚀钢筋混凝土板试验研究及分析［D］.南京:河海大学,2008.

［6］GB 10124-88 金属材料实验室均匀腐蚀全浸试验方法［S］.北京:中国标准出版社,1988.

［7］GB 50152-92 混凝土结构试验方法标准［S］.北京:中国建筑工业出版社,1992.

［8］GB 50010-2010 混凝土结构设计规范［S］.北京:中国建筑工业出版社,2011.