（内蒙古科技大学土木工程学院， 包头 014010）

［摘要］泡沫微晶玻璃砖是由陶瓷废料、粉煤灰、尾矿等工业废弃物为主要原料制作而成的，是一种轻质、高强、保温、可回收的新型的环保材料，可有效地缓解人地矛盾，促进人类社会的可持续发展。为了进一步推广该新型材料的应用，采用砌体基本力学性能试验方法，对三种不同混合砂浆条件下的泡沫微晶玻璃砖砌体进行了轴心抗压试验，其受压破坏过程及形态与烧结普通砖砌体相似。最后，提出了泡沫微晶玻璃砖砌体抗压强度平均值建议公式及弹性模量建议计算公式。

［关键词］泡沫微晶玻璃砖； 抗压强度； 弹性模量； 泊松比

中图分类号：TU502文献标识码：A文章编号：1002-848X(2016)15-0102-04

Experimental research on compressive strength of foam crystallized glass brick masonry

Li Fengge, Qin Xiaojun

(School of Civil Engineering, Inner Mongolia University of Science and Technology, Baotou 014010, China)

Abstract:Foam crystallized glass brick is mainly made from ceramic waste, fly ash, tailings and other industrial wastes. It is a new type of environmentally and friendly material with lightweight, high strength, thermal insulation and recyclability. It can effectively alleviate the contradiction between man and land and promote the sustainable development of human society. In order to further promote the application of this new material, axial compressive tests on foam crystallized glass bricks with three different mixed mortar conditions were carried out by using the basic mechanical property test method of masonry. The compression failure process and morphology were similar as that of common sintered brick masonry. Finally, the suggested formula for average value of the compressive strength of the foam crystallized glass brick was proposed and the suggested calculating formula for the elastic modulus was proposed.

Keywords:foam crystallized glass brick; compressive strength; elastic modulus; Poisson ratio