［摘要］对550MPa高强冷弯薄壁型钢帽型截面简支檩条和两跨连续檩条的受力性能进行了试验研究，27根简支檩条试件和24根两跨连续檩条试件的试验结果表明：厚度为0.48，0.60和0.75mm的简支和两跨连续檩条在高强钢材强度折减系数γ取0.8，厚度为1.00mm的檩条在γ取0.9时，理论承载力与试验结果吻合较好。
［关键词］高强冷弯薄壁型钢;帽型截面;简支檩条;连续檩条
Experimental study on bearing behavior of high strength cold-formed steel battens under bending
Liao Fangfang1, Zhang Wei2, He Baokang2, Wang Yanmin3(1 Tongji University, Shanghai 200092,China; 2 Xi′an University of Architecture and Technology, Xi′an 710055,China; 3 Bluescope Steel Building, Residential, Shanghai 201613, China)
Abstract:The bearing capacity behavior of 550MPa high strength cold-formed steel simple and continuous hat section battens under bending has been studied. The test results of 27 simple specimens and 24 continuous specimens show that when the strength reduction coefficientγ of high strength steel is determined as 0.8, the test results of specimens with thickness 0.48，0.60，and 0.75mm are close to the theoretical bearing capacity; whenγis determined as 0.9, the test results of specimens with thickness 1.00mm are close to the theoretical values.
Keywords:high strength cold-formed steel; hat section; simple batten; continuous batten
作者简介：廖芳芳，女，博士生。
参考文献
［1］周天华，周绪红，何保康，等. G550级高强薄板钢材的材性及应用［J］.建筑科学与工程学报，2005，22（2）：43-46.
［2］GB50018—2002冷弯薄壁型钢结构技术规范［S］.北京：中国计划出版社，2002.
［3］YU W W. Cold-Formed Steel Design,3nd Ed［M］. John Wiley & Sone, Inc. New York,2000.
［4］周天华，何保康，周绪红，等. 高强冷弯薄壁型钢轴压短柱受力性能试验研究［J］.建筑科学与工程学报，2005，22（3）：36-44.
［5］高强冷弯薄壁型钢TOPSPAN 40/61型檩条弯曲性能试验研究报告No.5［R］.西安建筑科技大学钢结构研究所，博思格建筑系统住宅部，2006.
［6］LYSAGHT Ｄ○R TOPSPAN TM 22/40/61［C］. BlueScope Steel (Shanghai) Co.,Limited. 25th Oct, 2005.