［摘要］使用埋设型KM系列应变传感器成功监测了处于模拟施工现场环境下，高性能混凝土柱早期自收缩变形特性，特别是混凝土浇注后24h的自收缩变形情况。从试验结果看，硬化前后24h高性能混凝土的自收缩变形增长最快，绝对变形值也比较大，24h自收缩值超过14d自收缩变形量的70%；而配筋混凝土试件由于配筋形成的钢骨架对自收缩的约束作用，其自收缩变形小于同等条件的素混凝土试件。监测和分析高性能混凝土结构早期的自收缩变形将对减少结构微裂纹、提高结构的稳定性有重要意义。
［关键词］高性能混凝土；早期自收缩；埋设型应变传感器
Early-age autogenous shrinkage experimental study of high performance concrete column under construction-site conditions
Yun Yingwei 1, He Pengli 1, Cai Yanhong 2(1 Civil Engineering Department, Luoyang Institute of Science and Technology, Luoyang 471023, China;2 State Key Laboratory of High Performance Ceramics and Superfine Microstructure, ShanghaiInstitute of Ceramics Chinese Academy of Science, Shanghai 200050, China)
Abstract:The early\|age autogenous shrinkage of HPC column under construction-site conditions is monitored  successfully, especially the first 24-hour deformation just after casting by KM100B strain transducer. The experimental results show that HPC autogenous shrinkage rapidly increases within first 24 hours just after HPC casting, and first-day autogenous shrinkage is 70% larger than the total one within 14 days. And the autogenous shrinkage of reinforced specimen is smaller than that of plain specimen due to restraint of reinforcing frame. Monitoring and analyzing early-age autogenous shrinkage of HPC will give significant reference to study the durability and permeability of HPC structures.
Keywords:high performance concrete; early-age autogenous shrinkage; embedded stain transducer
洛阳理工学院人才引进科研基金资助。
作者简介：贠英伟，博士研究生，讲师，Email:Yunyingwei1979@yahoo.com.cn。
参考文献
［1］TAZAWA E,MIYAZAWA S. Autogenous shrinkage of concrete and its importance in concrete technology［C］// Creep and Shrinkage of  Concrete. Proceedings of the 5th International RILEM. London:Symposium, E & FN Spon,1993: 59-168.
［2］AICTIN P C, NEVILLE A M, ACKER P. Integrated view of shrinkage deformation［J］. Concrete International,1997, 19 (9): 35-41.
［3］AICTIN P C Autogenous shrinkage measurement［Ｇ］//Autogenous Shrinkage of Concrete.E & FN Spon, 1999: 257-268.
［4］NFDA4英伟,张广峻,张百岁,等. FBG传感器监测高性能混凝土早期特性的试验研究［J］. 混凝土，2008(5)：124-127.
［5］朱永,陈伟民,封君,等.混凝土固化期收缩应变监测的光纤珐珀传感器［J］.土木工程学报,2001,34(5):24-28.
［6］Il YOUNG JANG,et al. The short term property monitoring for HPC columns by embedded FBG sensor［J］. Annual Report of Institute of Industrial Technology Kumoh National of Technology, 2007, 22: 31-42.
［7］GB/T50081—2002 普通混凝土力学性能试验方法标准［S］. 北京：中国建筑工业出版社，2002.
［8］HEDLUND H. Stresses in High Performance Concrete due to Temperature and Moisture Variations at Early Ages［D］. Lule, Sweden: Lule University of Technology, 1996.
［9］BYFORS J. Plain Concrete at Early Ages［R］.Swedish Cement and Concrete Research Institute Report,1980.