高温后合成纤维混凝土的强度试验研究
王岳华,丁一宁
摘 要
(大连理工大学海岸和近海工程国家重点实验室,大连 116024)
[摘要]研究了普通混凝土(NC)、聚丙烯纤维混凝土(PPFRC)和聚丙烯腈纤维混凝土(PANFRC)在常温及300,600,1 000℃高温后的抗压强度和抗折强度,分析了高温加热方式及加载条件不同的影响。研究表明,300 ℃高温下混凝土的劣化主要受升温速率的影响;600 ℃以上高温下混凝土的劣化主要受温度的影响。掺入低掺量的PP纤维和PAN纤维可缓解混凝土的高温劣化,从而提高高温后混凝土的抗压强度和背火面加载时的抗折强度。
[关键词]合成纤维;高温;抗压强度;抗折强度;聚丙烯纤维;聚丙烯腈纤维
Experimental research on strength of synthetic fiber reinforced concrete after high temperatures
Wang Yuehua, Ding Yining(The State Key Laboratory of Coastal and Offshore Engineering Dalian University of Technology, Dalian 116024, China)
Abstract:The compressive strength and the flexural strength of Normal Concrete(NC), Polypropylene Fiber Reinforced Concrete(PPFRC) and Polyacrylonitrile Fiber Reinforced Concrete (PANFRC) under normal temperature and after different high temperatures of 300℃, 600℃, 1 000℃ are investigated, and the influences of different high-temperature heating methods and loading conditions are analyzed. The results show that, the deterioration of concrete under high temperature of 300℃ is mainly influenced by heating rate, while the deterioration of concrete under high temperature upwards of 600℃ is mainly influenced by temperature. Mixing PP fiber or PAN fiber with low content can mitigate the high-temperature deterioration of concrete, with the result of improving the compressive strength of concrete after high temperature and also improving the flexural strength of concrete when loading on the unexposed surface after fire.
Keywords:synthetic fiber; high temperature; compressive strength; flexural strength; Polypropylene Fiber; Polyacrylonitrile Fiber
*国家自然科学基金资助项目(50278013)。
作者简介:王岳华,博士研究生,Email:yhwang78@hotmail.com。
参考文献
[1]KIRKLAND C J. The fire in the channel tunnel[J]. Tunnellingand Underground Space Technology, 2002, 17: 129-132.
[2]TAN G L. Fire fighting in tunnels[J]. Tunnelling and Underground Space Technology, 2002, 17: 179-180.
[3]KALIFA P, MENNETEAU F D, QUENARD D. Spalling and pore pressure in HPCat high temperatures[J]. Cement and Concrete Research, 2000, 30: 1915-1927.
[4]KALIFA P, CH?N?G, GALL? C. High-temperature behavior of HPC with polypropylene fibres from spalling to microstructure[J]. Cement and Concrete Research, 2001, 31: 14871499.
[5]鞠丽艳,张雄. 聚丙烯纤维对高性能混凝土高温性能的影响[J]. 建筑材料学报,2004,7(1).
[6]袁杰,吴波. PP纤维高强混凝土的和易性及高温后抗压强度的试验研究[J]. 混凝土,2001,(3).
[7]游有鲲,钱春香,缪昌文. 掺聚丙烯纤维的高强混凝土高温性能研究[J]. 江苏建筑,2003,(4).
下载地址

    你还没注册?或者没有登录?这篇论文要求至少是本站的注册会员才能阅读!

    如果你还没注册,请赶紧点此注册吧!

    如果你已经注册但还没登录,请赶紧点此登录吧!