［摘要］浇注了5个钢筋混凝土柱式大试件，养护三个月后通过电化学方法加速其锈蚀，得出了锈胀开裂时钢筋的锈蚀率。基于电化学锈蚀试验结果，并结合已有的试验资料，建立了考虑电化学锈蚀速度、相对保护层厚度及粗钢筋影响的锈裂模型, 该模型具有较强的通用性。
［关键词］钢筋混凝土；钢筋锈蚀；锈裂模型；电化学
Study on effect of testing condition on models of corrosioncracking of reinfor
ced concrete
Zheng Xiaoyan１， Wu Shengxing2(1 Nanjing Forestry University,Nanjing 210037, China; 2 Hehai University, Nanjing 210098, China)
Abstract:Five large size column-ype specimens were poured. After being cured for three months, these specimens were under accelerated corrosion by electro chemical method, and the corrosion rate of steel bar at the moment of concrete cracking had been obtained. A new model,which was based on comprehensive analysis of the testing results, was presented，in which, the effect of electrochemical corrosion velocity,large c/d and large diameter re-bar were considered by revision coefficient.The model is of great currency.
Keywords:reinforced concrete； steel corrosion； model of corrosion-cracking； electrochemistry
国家自然科学基金项目“钢筋混凝土结构锈裂损伤的参数识别与系统仿真评估”(50079002)。
作者简介：郑晓燕，博士，教授，Email:xyzh@njfu.edu.cn。
参考文献
［1］MOLINA  F J. Cover cracking as affection of bar corrosion: Part ⅡNumerical model［J］. Materials and Structures,1993, 26:932548.
［2］ROBERTS  M B, ATKINS C, et al. A proposed empirical corrosion model for reinforced concrete［J］. Structure and Building,I.C.E,2000, 140:111.
［3］徐善华，牛荻涛，陈新孝. 钢筋混凝土结构锈胀寿命分析［J］.建筑科学, 2002,18(5): 32-35.
［4］淡丹辉.基于模型的钢筋混凝土构件锈蚀裂缝的全过程非线性有限元分析［D］. 西安：西安建筑科技大学，1997.
［5］潘振华，牛荻涛，王庆森.钢筋锈蚀开裂条件的试验研究［J］.工业建筑,1999,29(5)：46-19.
［6］李海波，鄢飞，赵羽习，等.钢筋混凝土结构开裂时刻的钢筋锈胀力模型［J］.浙江大学学报，2000,34(4):415422.
［7］张伟平.混凝土结构的钢筋锈蚀损伤预测及其耐久性评估［D］.上海：同济大学，1999.
［8］郑晓燕. 锈蚀钢筋与混凝土动态粘结性能研究［D］. 南京:河海大学，2004.