［摘要］为研究角钢桁架型钢混凝土梁的纯扭性能，设计加载装置并完成了7个角钢桁架型钢混凝土梁在纯扭荷载作用下的静力试验，考虑了型钢配钢形式、型钢保护层厚度和混凝土强度等级3个变化参数。通过试验观察了试件的破坏形态，揭示其破坏机理，获取了扭矩-应变曲线、扭矩-扭转角曲线及相关特征点等，并分析各变化参数对其抗扭性能的影响，基于能量守恒定律，分析了在纯扭作用下试件的耗能和损伤规律。试验结果表明：角钢桁架型钢混凝土梁纯扭破坏时角钢受拉屈服、棱角处混凝土被压碎，具有良好的抗扭和耗能性能。适当增加型钢体积配钢率和混凝土强度等级均能有效提高角钢桁架型钢混凝土梁的抗扭和耗能性能，增加斜向腹杆效果更显著。增加型钢保护层厚度会降低其抗扭和耗能性能。同时损伤规律基本呈现前期较小、后期较大的特征。

［关键词］角钢桁架; 型钢混凝土梁; 纯扭; 抗扭性能; 损伤

中图分类号：TU317      文献标识码：A      文章编号：1002-848X(2014)09-0015-07

Pure torsional experiment and damage analysis of angle steel truss reinforced concrete beams

Wang Ni1, Chen Zongping1,2, Yan Liubin1, Chen Yuliang1

 (1 College of Civil Engineering and Architecture, Guangxi University, Nanning 530004, China; 2 Key Laboratory of Disaster Prevention and Structural Safety of China Ministry of Education, Guangxi University, Nanning 530004, China)

Abstract: To research pure torsional properties of angle steel truss reinforced concrete beams, loading device was designed and 7 specimens of angle steel truss reinforced concrete beams were tested in static load test under pure torsional loads. Three vary parameters were considered in the experiment such as steel disposition form, steel protective layer thickness and concrete strength grade. The failure patterns were observed and the failure mechanism was revealed. The torque-strain curves, torque-torsion angle curves and relevant feature points were obtained. The influence of each vary parameter on the torsional properties was analyzed. The energy dissipation and damage rule of pure torsional specimens were analyzed based on the law of conservation of energy. The results of experiment show that: failure pattern of angle steel truss reinforced concrete beams under pure torsional loads was that angle steel truss yields and concrete in the corner was crushed, which has better torsion resistance and energy dissipation properties. The increase of the volumetric percentage of steel and the concrete strength grade can improve torsion resistance and energy dissipation properties, effectively increase of oblique web member. The increase of steel protective layer thickness can reduce torsion resistance and energy dissipation properties. The characteristics of damage rule presents that damage index is smaller in the early stage and bigger in the late stage.

Keywords: angle steel truss; steel reinforced concrete beam; pure torsion; pure torsional property; damage

*国家自然科学基金项目(50908057，51268004)，广西科技攻关项目（桂科攻12118023-3），广西自然科学基金项目(2013GXNSFDA019025)。

通讯作者：陈宗平，博士，教授，博士生导师，Email:zpchen@gxu.edu.cn。

参考文献

［1］秦卫红，卫云亭，张连德. 钢筋混凝土压、弯、剪、扭构件抗扭性能的研究［J］. 西安冶金建筑学院学报，1993， 25（4）：367-374.

［2］王振东，李东杰. 钢筋混凝土纯扭构件截面尺寸效应的试验［J］. 哈尔滨工业大学学报：自然科学版，2006，38（8）：1374-1377.

［3］黄靓，鲁懿虬，徐紫鹏. 钢筋混凝土剪扭构件承载力可靠度分析［J］.工程力学，2012，24（4）：185-191.

［4］聂建国，唐亮，魏茂林. 钢混凝土组合梁扭转的组合作用分析［J］. 工业建筑，2008，38（3）：1-4.

［5］胡少伟. 组合梁抗扭分析与设计［M］. 北京：人民交通出版社，2004.

［6］倪勇. 新型外包钢-混凝土组合梁受扭性能试验研究［D］. 南京：东南大学，2007.

［7］傅传国，李玉莹，孙晓波，等. 预应力及非预应力型钢混凝土框架受力及抗震性能试验研究［J］.建筑结构学报，2010，31(8)：15-21.

［8］郑文忠，王琨. 型钢混凝土梁-角钢混凝土柱框架抗震性能试验研究［J］.土木工程学报，2011，44(3)：49-60.

［9］KANG T, KIM W,  KWAK Y. Shear testing of steel fiber-reinforced lightweight concrete beams without web reinforcement［J］. ACI Structural Journal, 2011,108(5): 553-561.［10］梁书亭，朱筱俊，张根俞. 型钢混凝土复合受力构件受扭性能的试验研究［J］.工业建筑，2010，40（11）：131-135.